Model | iPhone 14 Pro Max 2.5D HD | |
Material | Glass | Xuhong high aluminosilicate glass |
AB lamination | oca 125um | |
Base material 110um | ||
Anti-static Silicone 35um | ||
Fingerprint oil | Japanese Daikin fingerprint oil | |
With white PC back panel | Empty with ears(Thickness0.65mm) | |
Craftsmanship | Thickness | WindowsGlassThickness0.33mm Overall Thickness (without back plate) 0.60mm |
Transmittance(Glass) | ≥92% | |
Hardness | 9H | |
Tempering time | 4 hours | |
Inks | 1:1 (original phone color) | |
Test items | Criteria | |
Performance Testing | Trial patch test | The internal arc conformity is <0.06,Does not enter dust |
Good exhaust performance, strong adsorption, no bubbles | ||
No scratching on the edges,Does not affect the protective cover | ||
Seamless, good visual effect | ||
There is no white border on the screen | ||
Touch sensitivity test | After the product is attached to the phone, there should be no problems affecting the touch control. | |
Anti-static | The Silica gel layer has anti-static function to prevent static electricity from adsorbing dust, and the anti-static value is up to 10⁶-10⁹ | |
Transmission test | Transmittance≧92% | |
Toughness test | Can be bent 90° and U-shaped, not fragile edges | |
Drop ball test | Drop ball test:64G steel ball, 100CM impacts the center point three times without breaking. | |
Water drop angle test | Water drop angle ≥ 115°; after rubbing 5000 times with 1*1 0000# 1KG, the water drop angle is above 100° | |
Surface Pencil Hardness Test | Use Mitsubishi Pencil 9H with a load of 500g and draw 3 lines on the surface without scratches. |