Model | iPhone X/XS/11 Pro 3D HD | |
Material | Glass | Xuhong high aluminosilicate glass |
AB lamination | Use layers 270um | |
A side release film 50um | ||
B side release film 70um | ||
Fingerprint oil | Japanese Daikin fingerprint oil | |
With white PC back panel | Empty with ears(Thickness0.80mm) | |
Craftsmanship | Thickness | Glass thickness 0.36mm Arc height:0.68mm Overall Thickness (without back plate) 0.63mm |
Transmittance(Glass) | ≥92% | |
Hardness | 9H | |
Tempering time | 4 hours | |
Inks | 1:1 (original phone color) | |
Test items | Criteria | |
Performance Testing | Trial patch test | The internal arc conformity is <0.15,Does not enter dust |
Good exhaust performance, strong adsorption, no bubbles | ||
No scratching on the edges,Does not affect the protective cover | ||
Seamless, good visual effect | ||
There is no white border on the screen | ||
Touch sensitivity test | After the product is attached to the phone, there should be no problems affecting the touch control. | |
Transmission test | Transmittance≧92% | |
Toughness test | Can be bent 90° and U-shaped, not fragile edges | |
Drop ball test | Drop ball test:The 64G steel ball 60CM impacts the center point three times without breaking. | |
Water drop angle test | Water drop angle ≥ 115°; after rubbing 5000 times with 1*1 0000# 1KG, the water drop angle is above 100° | |
Surface Pencil Hardness Test | Use Mitsubishi Pencil 9H with a load of 500g and draw 3 lines on the surface without scratches. |